Nanofiltration Performance of Zinc Solution: Effects of Solution Chemistry

บทคัดย่อ

The effects of solution chemistry (i.e. solution pH and ionic strength) on nanofiltration systems
were investigated using a dead-end test cell at room temperature. An aromatic polyamide NF-90
membrane was chosen to determine the effects of zinc solution on nanofiltration fouling. The
experimental results revealed that solution flux decline was dependent on ionic strength and solution
pH. Flux decline conducted in ZnSO4 solution decreased for solution pH. At pH 6-8, flux solutions
showed higher flux decline than those of low solution pH, while zinc rejection exhibited higher rejection.
Increased ionic strength had a greater increase in flux decline. Zinc ion rejection was found to be
decreased with decreasing solution pH and increasing ionic strength. Solution pH of 6-8 had greater ion
rejection about 97% - 98%, whereas solution pH of 4 exhibited lower rejection approximately 85-86%.

ผลกระทบทางเคมีของสารละลาย เช่น ค่า pH และความแรงประจุของสารละลาย ต่อระบบนาโนฟิลเตรชัน ซึ่งได้
ทำการศึกษาด้วยชุดทดสอบเมมเบรนแบบไหลตามแนวดิ่ง (dead-end test cell) ณ อุณหภูมิห้อง เมมบรนชนิดอะโรเมติก
โพลีเอไมด์ NF-90 ได้เลือกนำมาใช้เพื่อศึกษาผลกระทบของสารละลายสังกะสีต่อการอุดตันในระบบนาโนฟิลเตรชัน ผลการ
ทดลองพบว่า
การลดลงของฟลักซ์ในสารละลายขึ้นอยู่กับความแรงประจุ และค่า pH ของสารละลาย การลดลงของฟลักซ์
สารละลาย ZnSO4 จะลดลงในสารละลายที่มีค่า pH ลดลง โดยพบว่าที่ pH 6-8 การลดลงของฟลักซ์ในสารละลายจะสูงกว่า
สารละลายที่มีค่า pH ที่ต่ำกว่า ขณะที่การกำจัดสังกะสีจะมีค่าการกำจัดที่สูงกว่า ความแรงประจุที่เพิ่มมากขึ้นส่งผลให้การลดลง
ของฟลักซ์เพิ่มมากขึ้น การกำจัดไอออนของสังกะสีลดลงเมื่อค่า pH ของสารละลายลดลงและเมื่อเพิ่มความแรงประจุ ค่า pH
ของสารละลายที่ 6-8 มีค่าการกำจัดไอออนโดยเฉลี่ย 97-98% ในขณะที่ที่ pH 4 มีค่าการกำจัดที่น้อยกว่า โดยเฉลี่ย 85-86%